Apparatus and methods for solar energy conversion using nanocoax structures

ABSTRACT

An apparatus and method for solar conversion using nanocoax structures are disclosed herein. A nano-optics apparatus for use as a solar cell comprising a plurality of nano-coaxial structures comprising an internal conductor surrounded by a semiconducting material coated with an outer conductor; a film having the plurality of nano-coaxial structures; and a protruding portion of the an internal conductor extending beyond a surface of the film. A method of fabricating a solar cell comprising: coating a substrate with a catalytic material; growing a plurality of carbon nanotubes as internal cores of nanocoax units on the substrate; oxidizing the substrate; coating with a semiconducting film; and filling with a metallic medium that wets the semiconducting film of the nanocoax units.

RELATED APPLICATIONS

This application claims the benefit of U.S. Provisional Application Ser. No. 60/711,004, filed Aug. 24, 2005, the entirety of which is hereby incorporated herein by reference for the teachings therein.

GOVERNMENT SUPPORT

The invention was supported, in whole or in part, by Contract No. DAAD 16-02-C-0037 from the U.S. Army Natick Soldier Systems Center. The Government has certain rights in the invention.

FIELD

The embodiments disclosed herein relate to the field of solar energy conversion using nano-optics, and more particularly to an apparatus and method for solar conversion using nanocoax structures.

BACKGROUND

Nano-optics is the study of optical interactions with matter structured into units of subwavelength (for visible light) dimensions. Nano-optics has numerous applications in optical technologies such as nanolithography, high-density optical data storage, photochemistry on a nanometer scale, solar cells, materials imaging and surface modification with subwavelength lateral resolution, local linear and nonlinear spectroscopy of biological and solid-state structures, quantum computing and quantum communication.

Solar cells using nano-optics are known in the art. At present, high efficiency can be achieved only in p-n junction photovoltaic (PV) cells with average aperture-area efficiency (AAE) of about 20-28%, and modules with average AAE of about 17%. In research-grade multijunction concentrators, efficiencies as high as about 39% have been reported. These are based on crystalline semiconductors, which are expensive. For standard crystalline silicon (c-Si) PV technology, not only is the material cost some 50% higher than that of thin film forms, but the cost for installation is high compared to flexible substrate PVs such as those made from amorphous silicon (a-Si). Inexpensive PV cells based on non-crystalline semiconductors have the following AAE's: a-Si about 12%; CdTe (cadmium telluride) about 16%; and CIS (copper indium diselenide) about 19%. See B. von Roedern, K. Zweibel, and H. S. Ullal, “The role of polycrystalline thin-film PV technologies for achieving mid-term market competitive PV modules,” 31st IEEE Photovoltaics Specialists Conference and Exhibition, Lake Buena Vista, Fla., Jan. 3-7, 2005.

The fundamental physics behind low efficiency of inexpensive cells is directly related to the difficulty in assuring simultaneously high photon absorption and charge collection efficiencies. Furthermore, for a-Si-based solar cells, the stabilized efficiency is typically about 15% lower than the initial value due to light-induced metastable defect creation, known as the Staebler-Wronski effect (SWE). D. L. Staebler and C. R. Wronski, “Reversible conductivity changes in discharge-produced amorphous Si,” Appl. Phys. Lett. 31, 292-294 (1977). Reducing the thickness and corrugating the surface of the active PV layer can improve efficiency significantly, but the low carrier mobility and lifetime product and the SWE are controlled by the band tails of the localized electronic states in the semiconductors, due to structural disorder. The structural disorder is a fundamental problem for all non-crystalline materials that reduces dramatically the diffusion length of the generated carriers.

Prior art attempts to manufacture solar cells using optical rectennas have had major difficulties in achieving large-scale metallic nanostructures at low cost. Recently, multi-walled carbon nanotubes (MWCNTs) were reported to behave like optical antennas that receive and transmit visible light incident upon them. These nanostructures were shown to be highly metallic with well aligned growth orientation. MWCNTs can also be fabricated at low cost in large scale on most conductive or semiconductive substrates by the well-established plasma-enhanced chemical vapor deposition (PECVD) method without using expensive and time-consuming state-of-the-art technologies, such as electron-beam lithography, which are unscalable but still inevitably being used by most other experimental approaches in this field. Thus, there is a need in the art to create a new class of very efficient, and low cost solar cells using nanocoax structures.

SUMMARY

An apparatus and method for solar conversion using nanocoax structures is disclosed herein.

According to aspects illustrated herein, there is provided a nano-optics apparatus for use as a solar cell comprising a plurality of nano-coaxial structures comprising an internal conductor surrounded by a semiconducting material coated with an outer conductor; a film having the plurality of nano-coaxial structures; and a protruding portion of the internal conductor extending beyond a surface of the film.

According to aspects illustrated herein, there is provided a solar cell comprising a metallic film having a top surface, a bottom surface; and a plurality of nano-coaxial structures comprising a metallic cylinder, filled with a dielectric material and having a central, concentric metallic core having a protruding portion extending beyond a top surface of the film.

According to aspects illustrated herein, there is provided a method of fabricating a solar cell comprising: coating a substrate with a catalytic material; growing a plurality of carbon nanotubes as internal cores of nanocoax units on the substrate; oxidizing the substrate; coating with a semiconducting film; and filling with a metallic medium.

According to aspects illustrated herein, there is provided a method of fabricating a solar cell comprising coating a substrate with a chromium layer; electrodepositing a catalytic transition metal on the coated substrate; growing an array of carbon nanotubes (CNTs) on the coated substrate; etching the chromium layer; coating the coated substrate and the array of CNTs with a dielectric material; and coating the coated substrate and the array of CNTs with a metal material.

BRIEF DESCRIPTION OF THE DRAWINGS

The presently disclosed embodiments will be further explained with reference to the attached drawings, wherein like structures are referred to by like numerals throughout the several views. The drawings are not necessarily to scale, the emphasis having instead been generally placed upon illustrating the principles of the presently disclosed embodiments.

FIG. 1A shows a schematic view of a plurality of nanocoax solar cell units of the disclosed embodiments embedded in a conductive matrix.

FIG. 1B shows a top view of a nanocoax solar cell unit of FIG. 1A.

FIG. 2A, FIG. 2B, and FIG. 2C each show a schematic view and an exemplary view of a nanocoax transmission line built around an aligned carbon nanotube. FIG. 2A shows a schematic view and an exemplary view of an aligned carbon nanotube. FIG. 2B shows a schematic view and an exemplary view of an aligned carbon nanotube after coating with a dielectric material. FIG. 2C shows a schematic view and an exemplary view of an aligned carbon nanotube after coating with a dielectric material and an outer conductor material.

FIG. 3 shows an array of nanocoax transmission lines built around aligned carbon nanotubes. FIG. 3A shows an exposed coaxial structure viewed by a scanning electron microscope (SEM). FIG. 3B shows a cross-section view of a single nanocoax transmission line viewed by a scanning electron microscope. FIG. 3C shows an energy dispersive x-ray spectroscopy (EDS) analysis of the composition of the coaxial layers showing concentration mapping for silicon (Si), chromium (Cr), and aluminum (Al). FIG. 3D shows a cross sectional view of an array of nanocoax solar cells with a concentrator.

FIG. 4A, FIG. 4B, and FIG. 4C show the results of optical experiments where white light was transmitted through an array of nanocoax transmission lines. FIG. 4A shows the surface topography of the array visible in reflected light with dark spots representing nanocoax transmission lines. FIG. 4B shows the surface topography of the same array as FIG. 4A visible in transmitted light with bright spots of the illuminating nanocoax transmission lines. FIG. 4C shows the surface topography of the array as a composition of the reflected light (FIG. 4A) and the transmitted light (FIG. 4B).

FIG. 5 shows a cross sectional view of nanocoax solar cells having non-straight conducting lines and a flexible matrix.

FIG. 6A shows a front perspective view of a nanocoax solar cell having multilayered structure of different bandgap semiconductors arranged in parallel layout.

FIG. 6B shows a front perspective view of a nanocoax solar cell having multilayered structure of different bandgap semiconductors arranged in serial layout.

FIG. 7 shows a front perspective view of a nanocoax solar cell with a concentrator extending from a top end of the nanocoax solar cell.

FIG. 8 shows a schematic image of a nano-optics apparatus that includes an array of carbon nanotubes, each tubule in the array consists of portions that protrude from a metallic film, known as an optical nano-antenna, and a portion that is embedded within the metallic film, known as a nano-coaxial transmission line.

FIG. 9A shows a three-dimensional configuration of a nano-optics apparatus synthesized in accordance with the presently disclosed embodiments.

FIG. 9B shows a scanning electron microscope (SEM) image of the nanorods used in the nano-optics apparatus of FIG. 9A.

FIG. 9C shows a transmission optical microscope image of the nano-optics apparatus of FIG. 9A.

FIG. 10A illustrates a method for synthesizing a nano-optics apparatus in accordance with the presently disclosed embodiments.

FIG. 10B illustrates a method for synthesizing a nano-optics apparatus in accordance with the presently disclosed embodiments.

FIG. 11 shows a graph of nano-antenna length versus radiation wavelength, at a maximum radar cross section (RCS) scattering amplitude.

FIG. 12A shows visible and SEM images (overlayed) of a section of a nano-optics apparatus synthesized in accordance with the presently disclosed embodiments.

FIG. 12B shows scanning electron microscopy (SEM) images of the nano-optics apparatus of FIG. 12A.

FIG. 13 shows a schematic image of a solar cell synthesized in accordance with the presently disclosed embodiments.

While the above-identified drawings set forth presently disclosed embodiments, other embodiments are also contemplated, as noted in the discussion. This disclosure presents illustrative embodiments by way of representation and not limitation. Numerous other modifications and embodiments can be devised by those skilled in the art which fall within the scope and spirit of the principles of the presently disclosed embodiments.

DETAILED DESCRIPTION

The embodiments disclosed herein relate to the field of solar energy conversion using nano-optics, and more particularly to an apparatus and method for solar conversion using nanocoax structures. A method of fabricating nanocoax solar cells is also disclosed. The following definitions are used to describe the various aspects and characteristics of the presently disclosed embodiments.

As referred to herein, “carbon nanotube”, “nanotube”, “nanowire”, and “nanorod” are used interchangeably.

As referred to herein, “nanoscale” refers to distances and features below 1000 nanometers (one nanometer equals one billionth of a meter).

As referred to herein, “single-walled carbon nanotubes” (SWCNTs) consist of one graphene sheet rolled into a cylinder. “Double-walled carbon nanotubes” (DWCNTs) consist of two graphene sheets in parallel, and those with multiple sheets (typically about 3 to about 30) are “multi-walled carbon nanotubes” (MWCNTs).

As referred to herein, “single-core coaxial transmission lines” (SCCTL) consists of one nanotube at the center. A “double-core coaxial transmission lines” (DCCTL) consists of two nanotubes at the center.

As referred to herein, CNTs are “aligned” wherein the longitudinal axis of individual tubules are oriented in a plane substantially parallel to one another.

As referred to herein, a “tubule” is an individual CNT.

The term “linear CNTs” as used herein, refers to CNTs that do not contain branches originating from the surface of individual CNT tubules along their linear axes.

The term “array” as used herein, refers to a plurality of CNT tubules that are attached to a substrate material proximally to one another.

The term “nanocoax” as used herein, refers to a nano-coaxial transmission line, which consists of a plurality of concentric layers. In an embodiment, the nanocoax has three concentric layers: an internal conductor, a semiconducting or dielectric coating around the core, and an outer conductor. Transmission of electromagnetic energy inside the coaxial line is wavelength-independent and happens in transverse electromagnetic (TEM) mode. In an embodiment, the internal conductor is a metallic core. In an embodiment, the outer conductor is a metallic shielding.

The term “transverse electromagnetic (TEM)” as used herein, refers to an electromagnetic mode in a transmission line for which both the electric and magnetic fields are perpendicular to the direction of propagation. Other possible modes include but are not limited to transverse electric (TE), in which only the electric field is perpendicular to the direction of propagation, and transverse magnetic (TM), in which only the magnetic field is perpendicular to the direction of propagation.

As referred to herein, a “catalytic transition metal” can be any transition metal, transition metal alloy or mixture thereof. Examples of a catalytic transition metal include, but are not limited to, nickel (Ni), silver (Ag), gold (Au), platinum (Pt), palladium (Pd), iron (Fe), ruthenium (Ru), osmium (Os), cobalt (Co), rhodium (Rh) and iridium (Ir). In an embodiment, the catalytic transition metal comprises nickel (Ni). In an embodiment, the catalytic transition metal comprises iron (Fe). In an embodiment, the catalytic transition metal comprises cobalt (Co).

As referred to herein, a “catalytic transition metal alloy” can be any transition metal alloy. Preferably, a catalytic transition metal alloy is a homogeneous mixture or solid solution of two or more transition metals. Examples of a catalytic transition metal alloy include, but are not limited to, a nickel/gold (Ni/Au) alloy, nickel/chromium (Ni/Cr) alloy, iron/chromium (Fe/Cr) alloy, and a cobalt/iron (Co/Fe) alloy.

The terms “nanotubes,” “nanowires,” “nanorods,” “nanocrystals,” “nanoparticles” and “nanostructures” which are employed interchangeably herein, are known in the art. To the extent that any further explanation may be needed, they primarily refer to material structures having sizes, e.g., characterized by their largest dimension, in a range of a few nanometers (nm) to about a few microns. In applications where highly symmetric structures are generated, the sizes (largest dimensions) can be as large as tens of microns.

The term “CVD” refers to chemical vapor deposition. In CVD, gaseous mixtures of chemicals are dissociated at high temperature (for example, CO₂ into C and O₂). This is the “CV” part of CVD. Some of the liberated molecules may then be deposited on a nearby substrate (the “D” in CVD), with the rest pumped away. Examples of CVD methods include but are not limited to, “plasma enhanced chemical vapor deposition” (PECVD), “hot filament chemical vapor deposition” (HFCVD), and “synchrotron radiation chemical vapor deposition” (SRCVD).

The presently disclosed embodiments generally relate to the use of nano-coaxial transmission lines (NCTL) to fabricate a nano-optics apparatus. The nano-optics apparatus is a multifunctional nano-composite material made of a metallic film having a top surface and a bottom surface and a plurality of coaxial structures (NCTLs). The NCTL comprises a metallic cylinder, filled with a dielectric material and having a central, concentric metallic core. Each NCTL has the central core extending beyond a surface of the film and an embedded portion that is within the film.

The presently disclosed embodiments increase harvesting efficiencies for photons and charge carriers by using a conductive medium, an elementary unit including a nanoantenna impedance matched to a nanocoaxial line filled with a photovoltaic (PV) active medium. While the nanoantenna provides efficient light collection, the nanocoaxial section traps the collected radiation, and assures its efficient conversion into electron-hole pairs. The coaxial symmetry yields high harvesting efficiency for both photons and charge carriers. The nanocoaxial line length can be made several microns long to assure high photon harvesting, and the nanocoaxial line width can be easily made small enough to provide high carrier harvesting between internal and external electrodes. The coaxial transmission line allows for subwavelength propagation, and thus a very small distance between electrodes. In fact, the distance between electrodes may be less than the carrier diffusion length without hampering the light propagation.

The presently disclosed embodiments work with any transmission line capable of the transverse electromagnetic (TEM) transmission. Such lines include, but are not limited to, the coaxial transmission line (i.e., a coax with a single core), the multi-core coaxial transmission line (multi-core coax), such as shown in FIG. 12B, view 41, and a stripline. A stripline is a transmission line consisting of two flat parallel metallic electrodes (strips), separated by a film of a dielectric. The width L of each electrode is larger than the radiation wavelength. The electrodes are distance d apart, which can be smaller than the radiation wavelength. In an embodiment, a nanocoax with a plurality of cores (multi-core) can be used to yield high harvesting efficiency for both photons and charge carrier. In an embodiment, a nanostripline (i.e., a stripline for visible light, which has d in the nanoscale) yields high harvesting efficiency for both photons and charge carriers.

Antennae are external resonators. The nanoantennas of the presently disclosed embodiments are broad resonators having large aspect ratios, that is their length l is much larger than their diameter d: for example, l>3 d. The bandwidth of the nanoantenna can be tuned to cover the entire solar spectrum. The nanoantennas described herein possess the directional characteristics of conventional antennas, proving that conventional, radio technology applies to the nano-optics systems in the visible frequency range.

The performance of the system of the presently disclosed embodiments will be comparable to that of c-Si, without its disadvantages, such as high material and installation costs. The system of the presently disclosed embodiments allows for even further improvements. With a multi-layer strategy, the photon energy can be matched to the semiconductor band gap, minimizing phonon losses, and further improving efficiency

FIG. 1A shows a schematic view of a nano-optics apparatus 100 including a plurality of nano-coaxial structures. The nanocoax structure includes an internal conductor 120 with an impedance-matched antenna 110 and a coaxial section 115 coated with a semiconducting material 180. The internal conductor 120 extends beyond the nanocoaxial structure forming the optical nano-antenna 110. An outer conductor 160 is an external coating of the coaxial section 115. A plurality of nanocoax structures are embedded in a conductive matrix 140. The nanocoax structure may be a nanocoax solar cell. The nano-optics apparatus is synthesized in accordance with the presently disclosed embodiments.

The internal conductor 120 may be a metallic core. Examples of metals for the internal conductor include but are not limited to, carbon fiber; carbon nanotube; pure transition metals such as nickel (Ni), aluminum (Al), or chromium (Cr); metal alloys, e.g. stainless steel (Fe/C/Cr/Ni) or aluminum alloys (Al/Mn/Zn); and metallic polymers. Other internal conductors are highly doped semiconductors, and semi-metals (metals with vanishingly small band gap, e.g. graphite). Those skilled in the art will recognize that the internal conductor may be other conducting materials known in the art and be within the spirit and scope of the presently disclosed embodiments.

The semiconducting material 180 has a band gap to maximize the absorption of light in the visible spectrum. Examples of semiconducting materials include, but are not limited to silicon (Si), cadmium telluride (CdTe), indium gallium phosphide (InGaP), gallium arsenide (GaAs), germanium (Ge), Cu(InGa)Se, GaP, CdS, indium antimonide (InSb), lead telluride (PbTe), Inl-x GaxN, and organic semiconductors (e.g., copper phthalocyanine (CuPc)). The semiconducting materials can be crystalline (periodic arrangement of atoms in macroscopic scale), polycrystalline (periodic arrangement of atoms in microscopic scale), or amorphous (aperiodic arrangement of atoms in macroscopic scale). Those skilled in the art will recognize that the semiconducting material may be other materials having band gap to maximize the absorption of light in the visible spectrum known in the art and be within the spirit and scope of the presently disclosed embodiments. The semiconducting material 180 may be uniform around the internal conductor 120 or the semiconducting material 180 may surround the internal conductor 120 in a non-uniform manner.

The outer conductor 160 may be a metal. Thus, the outer conductor 160 may take the form of a metallic cylinder. Examples of outer conductors include but are not limited to, carbon fiber; carbon nanotube; pure transition metals such as nickel (Ni), aluminum (Al), or chromium (Cr); metal alloys e.g. stainless steel (Fe/C/Cr/Ni) or aluminum alloys (Al/Mn/Zn); and metallic polymers. Other internal conductors are highly doped semiconductors, and semi-metals (metals with vanishingly small band gap, e.g. graphite). Those skilled in the art will recognize that the outer conductor may be other conducting materials known in the art and be within the spirit and scope of the presently disclosed embodiments.

FIG. 1B shows a top view of a nanocoax solar cell of FIG. 1A. In FIG. 1B, the diameter of the internal conductor 120 is 2r while the diameter of the outer conductor 160 is 2R. Those skilled in the art will recognize that the diameters can vary and be within the spirit and scope of the present invention.

FIG. 2A, FIG. 2B, and FIG. 2C each show a schematic view and an exemplary view of a nanocoax transmission line built around aligned carbon nanotube. FIG. 2A, FIG. 2B, and FIG. 2C show a single nanocoax structure selected from an array having a plurality of nanocoax structures. The schematic views show the three major steps for fabricating nanocoax solar cells. The exemplary views were taken using a scanning electron microscope (SEM) at a 30 degree angle to the sample surface.

FIG. 2A shows a schematic view and an exemplary view of an aligned carbon nanotube. The plasma-enhanced chemical vapor deposition (PECVD) method was used to grow vertically aligned, multiwalled, straight carbon nanotubes with an average length of about 5-6 μm using a nickel catalyst (FIG. 2A). The catalyst was electrodeposited on thin chromium layer (about 10 nm) sputtered on the top of a glass substrate.

FIG. 2B show a schematic view and an exemplary view of an aligned carbon nanotube after coating with a dielectric material. The nanotubes were coated with a dielectric layer of aluminum oxide (Al₂O₃). The dielectric layer has a thickness between about 100 nm to about 150 nm or thicker.

FIG. 2C shows a schematic view and an exemplary view of an aligned carbon nanotube after being coated with a dielectric material and an outer conductive material. The nanotubes were sputtered with about 100 nm to about 150 nm thick chromium layer as the outer conductor. In an embodiment, the outer conductor is thicker than 150 mn.

FIG. 3 shows an array of nanocoax transmission lines built around aligned carbon nanotubes. The array may have nanocoax transmission lines distributed uniformly or randomly on a substrate 190. The nanocoax transmission lines may be aligned in rows or unevenly distributed on the substrate 190. The substrate 190 may be transparent. The substrate 190 may be composed of a polymer, glass, ceramic material, carbon fiber, glass fiber or combinations thereof. Those skilled in the art will recognize that the substrate may be other materials known in the art and be within the spirit and scope of the presently disclosed embodiments.

An array of vertically aligned conductors (e.g., multiwalled carbon nanotubes or other nanowires/nanofibers) are grown or attached to the substrate. Next, the conductors are coated with appropriate dielectric or semiconducting material. The conductors are then coated with the metallic layer acting as the outer conductor.

An array of nanocoax transmission lines includes vertically aligned carbon nanotubes grown on glass substrate coated with a thin (about 10 nm) chromium layer. On this layer nickel catalyst for PECVD growth of nanotubes was deposited electrochemically. Then, nanotubes were coated with 150 nm of aluminum oxide and subsequently with 100 nm of chromium. The entire array of nanocoaxes was filled with spin-on-glass (SOG) which does not affect array functionality but allowed the top part of the nanocoaxes to be mechanically polished off. This way nanocoax cores could be exposed and they could work as wavelength-independent transmission lines. FIG. 3A shows an exposed coaxial structure viewed by a scanning electron microscope (SEM).

FIG. 3B shows a cross-section view of a single nanocoax transmission line viewed by a scanning electron microscope. FIG. 3B shows the internal structure of the nanocoax transmission line after polishing and being exposed.

FIG. 3C shows an energy dispersive x-ray spectroscopy (EDS) analysis of the composition of the coaxial layers showing concentration mapping for silicon (Si), chromium (Cr), and aluminum (Al). The dotted line in FIG. 3C corresponds to the position of the EDS linescan while three presented plots correspond to silicon (Si), chromium (Cr), and aluminum (Al) concentration along the scanned line. FIG. 3C shows that the concentration of silicon is highest in the silica (SiO₂) rich area. Similarly, highest chromium concentration is present in the region of metallic coating of nanocoax walls, and highest aluminum concentration is observed in the area of dielectric coating (Al₂O₃).

FIG. 3D shows a cross sectional view of an array of nanocoax solar cells with a concentrator, a concave indentation of the outer conductor around the nanocoax. The substrate is flexible. In an embodiment, the substrate 190 is aluminum (Al) foil, or other flexible metallic materials (copper, carbon fiber, steel, and similar materials). The substrate is coated with catalytic particles (e.g. Fe, Ni, Co) using wet chemical and electrochemical methods or conventional vacuum deposition techniques (e.g., sputtering, evaporation and similar techniques). Next, internal conductors 120 that are nanotubes are grown using techniques described herein (e.g., CVD, PECVD, and similar techniques), and the substrate area is exposed to oxygen, which affects only the exposed metallic substrate forming a dielectric layer 170. The thin film of semiconductor material 180 is grown using conventional deposition techniques (e.g. CVD and similar techniques). Finally, the substrate area is coated with a soft metallic layer 160 with appropriate wetting property against the semiconducting coating 180 such that a concentrator 185 is formed. The concentrator 185 is a concave meniscus adjacent to the coated internal conductors 120. In an embodiment, the metallic powder or liquid will be used to fill the inter-core spacing, followed by a thermal processing to form the concentrator 185. The concave meniscus region around each nanocoax unit acts as a light concentrator 185, an additional antenna collecting light from much larger area than the nanoantenna itself. The concentrators 185 allow the entire solar cell array to be fabricated with lower number of nanocoax units, while still maintaining very high efficiency. The concentrators 185 can be simply added to the solar cell array using techniques known in the art.

In an embodiment, the concentrator 185 self-forms in a conductive medium that poorly wets the surface of a semiconductor-coated nanocoax cores. A low-wetting metallic medium (e.g., a metallic powder or a liquid containing metallic particles) is deposited as the outer conductor 160, and thermal processing is used to control the wetting angle, i.e. the curvature of the concentrator 185. This will create the light concentrator 185, a convex depression around each nanocoax core.

FIG. 4A, FIG. 4B, and FIG. 4C show the results of optical experiments where white light was transmitted through an array of nanocoax transmission lines. FIG. 4A shows the surface topography of the array visible in reflected light with dark spots representing nanocoax transmission lines. FIG. 4B shows the surface topography of the same array as FIG. 4A visible in transmitted light with bright spots of the illuminating nanocoax transmission lines. FIG. 4C shows the surface topography of the array as a composition of the reflected light (FIG. 4A) and the transmitted light (FIG. 4A). There is a very good correlation between position of spots in illuminating nanocoax transmission lines both FIG. 4A and FIG. 4B. The transmitted light remains white (FIG. 4B), which suggest no cut-off frequency and wavelength independent transmission.

The nanocoax structures of the presently disclosed embodiments can be used as low-cost building blocks for mass scale fabrication of solar cell units. Solar cells could include non-aligned conductors produced in mass scale as nanocoax cores. FIG. 5 shows a cross sectional view of an embodiment of nanocoax solar cells having non-straight conductors and a flexible matrix. The non-straight conductors are not aligned with respect to adjacent conductors. Non-straight conductors can be used with any highly conductive nanotubes, nanowires, nanofibers or similar structures.

An example of non-straight conductors can be carbon nanotubes grown by thermal-CVD (chemical vapor deposition) technique. The internal conductor could be then chemically multi-coated with appropriate semiconductors of desired bandgaps and eventually metallized to finalize coaxial structure. FIG. 5 illustrates the non-straight conductor. Non-straight conductors 120, multicoated with semiconductors 180 a, 180 b, 180 c of appropriate bandgaps, and metallized on the surface with the outer conductor 160 are embedded into a conductive and flexible medium 145 (e.g., conductive paint or polymer). The protruding section 110 is exposed (e.g., by etching) and a thin layer of dielectric material 170 is deposited in the top of this structure. Then, a second, transparent conductor (e.g., indium tin oxide or another conductive polymer) is applied. A first contact 172 is adjacent to protruding sections 110 and above the dielectric layer 170. A second contact 174 is adjacent to the end of the internal conductor 120 opposite the protruding section 110, and the second contact 174 is in the conductive medium 145. In an embodiment, antenna sections would be non-aligned, randomly positioned, randomly tilted, and with various lengths. The non-straight and randomly positioned nanocoax transmission lines would dramatically improve collection efficiency by capturing the incoherent and broadband, unpolarized solar radiation.

In an embodiment, semiconductors having different bandgaps are used inside the nanocoax section to improve photon absorption efficiency. Better matching the semiconductor bandgap with incoming photon energy, yields improved energy conversion efficiency of nanocoax-based solar cells. The semiconducting material can be deposited along the internal conductor in a parallel configuration (FIG. 6A) or a serial configuration (FIG. 6B). FIG. 6A shows a front perspective view of a nanocoax solar cell having multilayered structure of different bandgap semiconductors 180 a, 180 b arranged in parallel layout. FIG. 6B shows a front perspective view of a nanocoax solar cell having multilayered structure of different bandgap semiconductors 180 a, 180 b, 180 c arranged in serial layout. Semiconductors having different bandgaps results in more efficient photon absorption because the various energies of collected photons would be better matched with the semiconductor bandgaps.

In an embodiment, a concentrator 185 extends from a top end of the nanocoax solar cell to enhance photon collection efficiency. FIG. 7 shows a front perspective view of a nanocoax solar cell with the concentrator 185 extending from a top end of the nanocoax solar cell. The concentrator 185 is a conical section extending from a top end of the nanocoax for improved photons collection. The concentrator 185 is a horn antenna, and could have variety of shapes known in the microwave technology art. The concentrator 185 may have shapes including but not limited to parabolically sloped walls or straight, conical walls or similar shapes. The concentrator 185 may be metallic. The concentrator 185 may be fabricated from any highly conductive material including but not limited to a metal, metal alloy, highly doped semiconductor, conductive polymer and other conductive materials. The concentrator 185 could be an integral part of the outer conductive layer of each nanocoax. The concentrator 185 could be an attachment fabricated separately on the top of the nanocoax. The concentrator 185 can be implemented by employing a “non-wetting” conductive medium that would poorly wet the surface of a semiconductor-coated nanocoax cores to create a convex depression around each nanocoax core, as shown in FIG. 3D.

A method of fabricating a solar cell comprises coating a substrate with a catalytic material; growing a plurality of carbon nanotubes as internal cores of nanocoax units on the substrate; oxidizing the substrate; coating the substrate with a semiconducting film; and filling with a metallic medium that wets the semiconducting film of the nanocoax units.

A nanocoax solar cell can be fabricated using the method outlined below or similar methods. A flexible, metallic substrate such as a aluminum (Al) foil is coated with catalytic material (e.g., Ni) by any suitable technique including but not limited to wet chemical deposition, electrochemical deposition, CVD, sputtering, evaporation and similar techniques. The processed substrate is used for a catalytic growth of carbon nanotubes or any other suitable nanorods/nanowires as internal conductors and cores of nanocoax units. The growth of the nanotubes can be performed by any appropriate technique including CVD or PECVD and similar techniques. After growing of the nanotubes, the remaining exposed surface of the substrate, i.e. the area free of nanotubes/nanowires, is oxidized to fabricate the dielectric layer between the substrate and the outer conductor. Then, the entire system can be coated with a semiconducting layer by any suitable technique (e.g. CVD, electro-chemical deposition, and similar techniques), and eventually filled with a metallic medium (e.g. tin (Sn) powder). The metallic medium should be selected and processed to obtain a weak wetting contact between the metallic medium and the outer conductor of the nanocoax. The metallic medium can be deposited by any conventional technique, e.g. spraying, painting, spin-coating, CVD, evaporation, sputtering, and similar techniques.

The presently disclosed embodiments generally relate to the use of nano-coaxial transmission lines (NCTL) to fabricate a nano-optics apparatus. The nano-optics apparatus is a multifinctional nano-composite material made of a metallic film having a top surface and a bottom surface and a plurality of cylindrical channels filled with a dielectric material. An array of nanorods penetrate the metallic film through the plurality of cylindrical channels. The array of nanorods has a protruding portion that extends beyond a surface of the metallic film and an embedded portion that is within the metallic film. The protruding portion acts as a nano-antenna and is capable of receiving and transmitting an electromagnetic radiation at a visible frequency. The embedded portion acts as a nano-coaxial transmission line (CTL) and allows for propagation of external radiation with a wavelength exceeding the perpendicular dimensions of the nanorod.

The nano-optics apparatus can concentrate light, and therefore enhance a field up to about 10³ times. The array of optical nano-antennas, with nano-CTL embedded in a metallic film, effectively compresses light into nanoscopic dimensions. The nano-antennas are capable of receiving and transmitting an electromagnetic radiation at the visible frequencies. The extreme compression of light in the nano-CTL leads to an asymmetric tunneling of electrons between the electrodes of the nano-CTL, and thus provides a rectifying action at the light frequencies, and thus conversion of the light into a direct current (DC) voltage. This property leads to a new class of efficient, and low cost rectenna solar cells. The extreme compression of light in the nano-CTL is quick, and is not limited by the usual parasitic capacitances that make the conventional diode rectification inefficient, if not impossible, at the light frequencies.

FIG. 8 shows a schematic image of a nano-optics apparatus 100 synthesized in accordance with the presently disclosed embodiments. The nano-optics apparatus 100 has an array of metallic nanorods 120 that penetrate a metallic film 140 through cylindrical channels 160 filled with a dielectric material 180. Each nanorod 120 has an optical nano-antenna 110 that protrudes from each surface of the metallic film, and a nano-coaxial transmission line (CTL) 115 that is embedded within the metallic film.

FIG. 9A shows a three-dimensional image of a basic structure configuration of a nano-optics apparatus 200 synthesized in accordance with the presently disclosed embodiments. Nanorods 220 extending beyond a metallic film 240 act as nano-antennas 110, capable of receiving and transmitting an electromagnetic radiation at the visible frequencies. The incoming light, collected by an array of the optical nano-antennas 110, is compressed into nanoscopic channels of the coaxial transmission lines (cables) 115, and is subsequently decompressed (and reemitted) on the opposite side of the film by the nano-antenna 110 segments. The nano-antennas 110 possess the directional characteristics of conventional antennas, proving that conventional, radio technology applies to the nano-optics apparatus 200 in the visible frequency range. The conventional coaxial cables for light may also be developed. An advantage of using the nano-coaxial cables 115 is that they do not have a cut-off frequency (in contrast to waveguides), i.e. the nano-coaxial cables 115 allow for propagation of radiation with wavelength exceeding their perpendicular dimensions. The purpose of using the nano-coaxial cables 115 in the nano-optics apparatus 200 is to channel, and compress the external radiation into the confined space between the internal and external electrodes. The degree of this compression can be estimated as follows. A matched antenna collects radiation from an area of the order of λ². Subsequently, this radiation energy can be efficiently transferred into the coaxial transmission line, where it compresses into an area of π(R²−r²), thus the power compression factor is of the order of λ²/π(R²−r²). By employing nanorods 120 with a radius r≈5 nm, and using a perpendicular dimension R≈20 nm, the power compression factor of the order of several hundreds in the visible range is possible.

The electric field inside the coaxial line varies as 1/ρ, where ρ is the radial distance from the center, and thus can be made very large for small r. It can be shown, that the electric field enhancement is of the order of λ/ρ, and thus is of the order of about one hundred in the visible range at the nanorod 220 with r≈5 nm. An additional, dramatic field enhancement can be achieved by using nanorods 220 with active plasmon resonances in the range of operation, e.g. gold or silver. Calculations show that there is an additional, resonant enhancement by factor as high as 10⁴ due to the plasmon (Mie) resonances. These results explain the giant field enhancements deduced from the Raman experiments. The total field enhancement can be expected to be as high as 10⁶ to 10⁷, and therefore high enough to trigger nonlinear processes in the dielectric of the coaxial cable, leading to the desired switching-off the transmitted electromagnetic energy. To illustrate the effect, consider a modest enhancement of 10⁵, achievable with the plasmonic nanorods 220. The corresponding field intensity is about 2 V/μm for an incoming flux of 1 W/m², which is about 1000 times smaller than that of a typical laser pointer. Such field intensities are sufficient to cause a field emission from typical nanorods 220.

FIG. 9B shows a scanning electron microscope image showing the relative characteristics of the nanorods 220 of FIG. 9A. The nanorods 220 are aligned linearly in the nano-optics apparatus 200. FIG. 9C shows a transmission electron microscopy image of the nano-optics apparatus 200 of FIG. 9A. In the nano-optics apparatus 200 of FIG. 9A, only the top half of the nano-optics apparatus 200 was etched during fabrication, the bottom half was not etched. This results in just the top half portion having transmitted light, as seen in the transmission optical microscopy image of FIG. 9C.

FIG. 10A shows an exemplary method for synthesizing the nano-optics apparatus 100. In step 1, chromium is sputtered onto a glass substrate, typically at a thickness of about 15 nm. A selected thickness of catalytic transition metal (for example nickel) is electrodeposited onto the chromium glass followed by carbon nanotube growth, as shown in steps 2 and 3. Plasma enhanced chemical vapor deposition (PECVD) is used to etch the chromium layer, as shown in step 4. Typical PECVD lasts about an hour. A dielectric (or semiconductor) material (for example SiO_(x), where 0≦x≦2) is sputtered on the substrate, as shown in step 5. Those skilled in the art will recognize that the sputtered material may be made of any material having a specific function as required by an application of the nano-optics apparatus and still be within the scope and spirit of the presently disclosed embodiments. Typically, the dielectric material is coated to yield a thickness of about 100 nm. Aluminum is then sputtered followed by spin-coating of polymethylmethacrylate (PMMA) and baking at about 180° C. for about 40 min, as shown in steps 6 and 7. Typically, about 400 nm of aluminum is sputtered. In step 8, electrochemical etching of the aluminum layer on the tips of the nanorods 120 is accomplished at about 25 min in about 20% H₂SO₄, 4.0 V, sample as anode, a platinum electrode as cathode. In this example, only the bottom half of the sample was etched, resulting in just that portion having transmitted light, as seen in the transmission electron microscopy image.

FIG. 10B shows an alternative method for synthesizing the nano-optics apparatus 100. In step 1, chromium is sputtered onto a glass substrate, typically at a thickness of about 15 nm. A selected thickness of catalytic transition metal (for example nickel) is electrodeposited onto the chromium glass followed by carbon nanotube growth, as shown in steps 2 and 3. Plasma enhanced chemical vapor deposition (PECVD) is used to etch the chromium layer, as shown in step 4. Typical PECVD lasts about an hour. A dielectric (or semiconductor) material (for example SiO_(x), where 0≦x≦2) is sputtered on the substrate, as shown in step 5. Those skilled in the art will recognize that the sputtered material may be made of any material having a specific function as required by an application of the nano-optics apparatus and still be within the scope and spirit of the presently disclosed embodiments. Typically, the dielectric material is coated to yield a thickness of about 100 nm. Aluminum is then sputtered onto the coated substrate, as shown in step 6. Typically, about 400 nm of aluminum is sputtered. In step 7, the tips of the nanotubes are removed by polishing. In step 8, electrochemical etching of the aluminum layer on the tips of the nanorods 120 is accomplished at about 25 min in about 20% H₂SO₄, 4.0 V, sample as anode, a platinum electrode as cathode.

FIG. 11 shows results demonstrating the antenna action of an array of nanorods 120 in the visible frequency range. Both, the polarization, as well as, the nano-antenna length effects are shown in the radar cross section (RCS) type of experiment, in which an external radiation is reflected/scattered by an aperiodic array of nanorods 120, in excellent agreement with the antenna theory. The main section shows the nano-antenna length versus radiation wavelength, at a maximum RCS scattering amplitude. The upper right image in FIG. 11 shows an image of the sample with interference colors (from left to right) due to gradually changing nanorod 120 length. The lower right image in FIG. 11 shows the scanning electron microscope image of the nanorods 120.

FIG. 12A shows a visible image of a section of a nano-optics apparatus 100 synthesized in accordance with the presently disclosed embodiments. The nano-CTLs 115 have been illuminated from behind with green and red lasers. Both green and red light is guided through the nano-CTLs 115. Each active nano-CTL 115 is surrounded by a green halo. Smaller red light spots are also visible. FIG. 5B shows the corresponding SEM close-up (top view) of the numbered nano-CTLs 115. Nano-CTL number 37 and number 47 are single core, while number 41 and number 48 are double core. Nano-CTL number 37 consists of a CNT core, coated with Si, located coaxially inside a cylindrical canal penetrating an Al film. An air gap (the dark ring) separates the Si coated CNT from the Al wall. As seen in FIG. 12B, the air gap is much thinner (˜100 nm) than the wavelength of the radiation (˜550 nm for green and 650 nm for red). Thus, the subwavelength action of the nano-CTL has been demonstrated.

In an embodiment, the nano-optics apparatus can be used as a solar cell as shown in FIG. 13. The asymmetric inter-electrode electron tunneling in the nano-CTLs (shown generally at 650) is the rectifying mechanism for a solar cell battery 600. The tunneling is asymmetric since the maximum field is always at the inner electrode. Thus the electrons tunnel from the inner to the outer electrode. For a proper chosen dielectric 680 (semiconductor) one can minimize band offsets at the metal-dielectric interfaces. This will eliminate any charge accumulation in the dielectric, and thus will make the field induced band bending, and the resulting tunneling a quick process. The solar radiation 620 enters the nano-CTLs 650 via a nano-antenna segment 630 of a nanorod 640. A sufficiently large field will trigger the tunneling resulting in negative charge accumulation on the outer electrodes. The inner electrodes can be connected providing the positively charged battery terminal.

A nano-optics apparatus for use as a solar cell comprises a plurality of nano-coaxial structures comprising an internal conductor surrounded by a semiconducting material coated with an outer conductor; a film having the plurality of nano-coaxial structures; and a protruding portion of the an internal conductor extending beyond a surface of the film.

A method of fabricating a solar cell comprises coating a substrate with a chromium layer; electrodepositing a catalytic transition metal on the coated substrate; growing an array of carbon nanotubes (CNTs) on the coated substrate; etching the chromium layer; coating the coated substrate and the array of CNTs with a dielectric material; and coating the coated substrate and the array of CNTs with a metal material.

All patents, patent applications, and published references cited herein are hereby incorporated by reference in their entirety. It will be appreciated that various of the above-disclosed and other features and functions, or alternatives thereof, may be desirably combined into many other different systems or applications. Various presently unforeseen or unanticipated alternatives, modifications, variations, or improvements therein may be subsequently made by those skilled in the art which are also intended to be encompassed by the following claims. 

1. A nano-optics apparatus for use as a solar cell comprising: a plurality of nano-coaxial structures comprising an internal conductor surrounded by a semiconducting material coated with an outer conductor; a film having the plurality of nano-coaxial structures; and a protruding portion of the an internal conductor extending beyond a surface of the film.
 2. The nano-optics apparatus of claim 1 wherein film is metallic.
 3. The nano-optics apparatus of claim 1 wherein film is non-metallic.
 4. The nano-optics apparatus of claim 1 wherein the protruding portion acts as a nano-antenna for receiving and transmitting an electromagnetic radiation into an interior of the nano-coaxial structures at a visible frequency.
 5. The nano-optics apparatus of claim 4 wherein the nano-antenna compresses light into nanoscopic dimensions of the nano-coaxial structure.
 6. The nano-optics apparatus of claim 1 wherein a convex indentation in the film around the protruding portion acts as a concentrator of an electromagnetic radiation.
 7. The nano-optics apparatus of claim 6 wherein the concentrator compresses light at an entrance to the nano-coaxial structure.
 8. The nano-optics apparatus of claim 1 wherein the nano-coaxial structures acts as a nano-coaxial transmission line (NCTL) for propagation of external radiation with a wavelength exceeding the perpendicular dimension of the internal conductor.
 9. The nano-optics apparatus of claim 1 wherein plurality of nano-coaxial structures are carbon nanotubes.
 10. The nano-optics apparatus of claim 1 wherein the semiconducting material is a dielectric material with a formula Al₂O₃.
 11. The nano-optics apparatus of claim 1 wherein the plurality of nano-coaxial structures compresses the external radiation into a space between an internal electrode and an external electrode.
 12. The nano-optics apparatus of claim 4 wherein the light is solar radiation.
 13. A solar cell comprising: a metallic film having a top surface, a bottom surface; and a plurality of nano-coaxial structures comprising a metallic cylinder, filled with a dielectric material and having a central, concentric metallic core having a protruding portion extending beyond a top surface of the film.
 14. The solar cell of claim 13 wherein the protruding portion is a nano-antenna for receiving and transmitting a radiation at a visible frequency.
 15. The solar cell of claim 13 wherein the protruding portion compresses solar radiation into nanoscopic dimensions.
 16. The solar cell of claim 13 wherein plurality of nano-coaxial structures are a nano-coaxial transmission lines (NCTL) for propagation of external solar radiation with a wavelength exceeding the perpendicular dimension of the core.
 17. A method of fabricating a solar cell comprising: coating a substrate with a catalytic material; growing a plurality of carbon nanotubes as internal cores of nanocoax units on the substrate; oxidizing the substrate; coating with a semiconducting film; and filling with a metallic medium.
 18. The method of claim 17 wherein the substrate is flexible aluminum foil.
 19. The method of claim 17 wherein the catalytic material is nickel.
 20. The method of claim 17 wherein the metallic medium wets the semiconducting film of the nanocoax.
 21. A method of fabricating a solar cell comprising: coating a substrate with a chromium layer; electrodepositing a catalytic transition metal on the coated substrate; growing an array of carbon nanotubes (CNTs) on the coated substrate; etching the chromium layer; coating the coated substrate and the array of CNTs with a dielectric material; and coating the coated substrate and the array of CNTs with a metal material.
 22. The method of claim 21 further comprising applying a polymethylmethacrylate to the coated substrate.
 23. The method of claim 21 further comprising polishing the coated substrate to expose the CNTs. 